Plastics Technology Laboratories  
 

Dielectric Strength

High Voltage and Current Dielectric Strength
Cabinet
ASTM D149
IEC 80243

Click on the picture for a larger view

Dielectric Voltage Arc

Scope:
Dielectric Strength is a measure of the electrical strength of a material as an insulator. Dielectric strength is defined as the maximum voltage required to produce a dielectric breakdown through the material and is expressed as Volts per unit thickness. The higher the dielectric strength of a material the better its quality as an insulator.

Test Procedure:
There are three basic procedures that can be used to determine the dielectric strength of an insulator. These procedures are the short-time method, the slow rate-of-rise method and the step-by-step method. Each of these three methods has the same basic set-up, which consists of the test specimen placed between two electrodes in air or oil.

For the most common test, the short-time method, voltage is applied across the two electrodes and raised from zero to dielectric breakdown at a uniform rate. Breakdown is when an electrical burn-through punctures the sample, or decomposition occurs in the specimen. The rate of voltage rise is determined by the time it takes the sample to reach dielectric breakdown.

The slow-rate-of rise method starts at 50% of the breakdown voltage as determined by the short-time-method and is increased at a uniform rate.

The step-by-step method starts at 50% of the short-time-test then voltage is increased at equal increments for a specified time period until breakdown. The test is sometimes performed in oil to prevent arcing from the electrode to the ground.

Specimen size:
The recommended specimen type for this test is a 4 inch plaque or larger. Any specimen thickness can be used, however the most common thickness is between 0.8 to 3.2 mm (0.032 to 0.125 inch). Specimens over 2 mm thick are typically tested in oil to decrease the chance of flashover before breakdown.

Data:
Dielectric strength is calculated by dividing the breakdown voltage by the thickness of the sample. The data is expressed in Volts/mil. The location of the failure is also recorded. A higher dielectric strength represents a better quality of insulator.

Equipment Used:
Hipotronics Dielectric Test Set
Electrodes


Intertek PTL Overview
Testing
Quality
Contact Us
Services & Tech Info
Industry Segments
Industry Segments

Search PTLI.com

**Please note that this test description is intentionally generic in nature and aimed at providing a descriptive summary to enhance test understanding. For more information please contact a Intertek PTL Technical Representative at . Due to copyright restrictions, we are not able to provide copies of standards. Standards can be obtained from appropriate standards authorities.

Back to Testlopedia